| Description |
Single componentnitro-cellulose based finish paint.
|
| Application Areas |
Used in metal industry, machinery, and furniture industry.
|
| Storage |
Should be stored in cool, well ventilated, and prevented from high temperature places.
|
| Package |
5 lt / 20 lt
|
 |
| Color |
RAL Scale
|
| Solid Matterial (volume) |
% 48 (+/- 2)
|
| Density |
1,1 - 1,2 gr/cm3
|
| Drying Time |
Depends on air circulaiton, environment temperature, film thickness and the number of coats applied.
|
| Flash Point |
30° C
|
| Brilliance |
Good
|
| Color Endurance |
Good
|
 |
| Mixture |
% 30 - % 35
|
| Thinner / Cleaning Solvent |
Extra cellulosic thinner
|
| Airless Pistol Data |
Hydrolic Pressure
(At the jet) |
: 15 Mpa |
| Jet |
: 0,38 - 0,53 mm |
| Spraying Angle |
: 40° - 80° |
| Filter |
: Should be clean. |
|
|
|
 |
| Surface Preparation |
Cleaned Surfaces must be oil, dirt and rust free.
|
| Application Conditions |
Surface temperature must be at least 3° C higher than the air condensation temperature.
|
| Recommended Painting System |
Cellulosic undercoat: 1x40 micron Cellulosic paint: 1x40 micron
|
| Working Conditions |
Should be used in well ventilated places by spraying. Follow S2 and S7 instructions.
|
| Application Method |
Applied with air or airless pistol.
|
|
Film Thickness
(Micron/coat) |
Theoretical
Spreading |
| Dry |
Wet |
(m2/lt) |
| Applicable Film Thickness |
|
|
|
| Recommended |
40-60 |
75-80 |
10 |
| Surface Temperature |
Surface Drying |
Hard Drying 2 |
Second Coat |
Coat 3 |
| Min. |
Max. |
20° C
|
3,5 minutes
|
1 hours
|
|
|
|
|