Very high quality finish paint that does not lose its brilliance ang strength very long time against Sunshine, acids, salts, oils, and physical impacts. After wet application on metal Surfaces, it gains hardening amd final drying by heat treatment.
|
|
 |
|
|
 |
| Description |
Ure-melamine resin based, furnace procesed finish paint.
|
| Application Areas |
Applied in metal industry.
|
| Storage |
Should be stored in cool, well ventilated, and prevented from high temperature places.
|
| Package |
20 lt
|
 |
| Color |
RAL Scale
|
| Solid Matterial (volume) |
% 50 (+/- 2)
|
| Density |
1,2 - 1,3 gr/cm3
|
| Drying Time |
Depends on air circulaiton, environment temperature and film thickness.
|
| Flash Point |
30° C
|
| Brilliance |
Glossy
|
| Color Endurance |
Good
|
 |
| Mixture |
% 30
|
| Thinner / Cleaning Solvent |
Furnace paint thinner
|
| Airless Pistol Data |
Hydrolic Pressure
(At the jet) |
: 15 Mpa |
| Jet |
: 0,38 - 0,53 mm |
| Spraying Angle |
: 40° - 80° |
| Filter |
: Should be clean. |
|
|
|
 |
| Surface Preparation |
Surfaces should be well cleaned, and oil, dirt and rust free.
|
| Application Conditions |
Surface temperature must be at least 3° C higher than the air condensation temperature.
|
| Recommended Painting System |
Furnace undercoat paint: 1x40 micron (dry film)
|
| Working Conditions |
Should be used in well ventilated places by spraying. Follow S2 and S7 instructions.
|
| Application Method |
Applied with air or airless pistol.
|
|
Film Thickness
(Micron/coat) |
Theoretical
Spreading |
| Dry |
Wet |
(m2/lt) |
| Applicable Film Thickness |
|
|
|
| Recommended |
20-30 |
50-70 |
12,7 |
| Surface Temperature |
Surface Drying |
Hard Drying 2 |
Complete Curing |
Second Coat |
5° C
10° C
23° C
|
60 minutes
60 minutes
30 minutes
|
4 hours
3 hours
3 hours
|
6 hours
24 hours
12 hours
|
36 hours
24 hours
12 hours
|
|
|
|