| Description |
Two component transparent varnish.
|
| Application Areas |
Applied on concrete and metal Surfaces.
|
| Storage |
Should be stored in cool, well ventilated, and prevented from high temperature places.
|
| Package |
20 lt CompA / 5 lt CompB
|
 |
| Color |
Red
|
| Solid Matterial (volume) |
% 50 (+/- 2)
|
| Density |
0,9 - 1,1 gr/cm3
|
| Drying Time |
Depends on air circulaiton, environment temperature, film thickness and the number of coats applied.
|
| Flash Point |
25° C (+/- 2)
|
| Brilliance |
Glossy
|
 |
| Mixture |
5 volume CompA + 1 volume CompB
|
| Karıştırma Süresi |
30 minutes before usage
|
| Mixture Applicable For |
8 hours (Decreases at high temperatures)
|
| Airless Pistol Data |
Hydrolic Pressure
(At the jet) |
: 15 Mpa (150kg/cm2) |
| Jet |
: 0,33 - 0,46 mm |
| Spraying Angle |
: 40° - 80° |
| Filter |
: Should be clean. |
|
|
|
 |
| Surface Preparation |
The Surface must be well cleaned, dry, and oil or petroleum products or other dirty material free.
|
| Application Conditions |
Surface temperature must be at least 3° C higher than the air condensation temperature. When applied on concrete the concrete should not contain more than 4% Su.
|
| Recommended Painting System |
For a transparent look: Epoxy clear varnish as dust preventing coat
For a colored finish: 1-2x40 micron epoxy clear varnish
|
| Working Conditions |
Zinc enriched undercoat: 1x25 micron
Finish paints can be chlore rubber, vinyl, acrylic or epoxy paints.
|
| Application Method |
Applied with airless pistol, brush, or roller.
|
|
Film Thickness
(Micron/coat) |
Theoretical
Spreading |
| Dry |
Wet |
(m2/lt) |
| Applicable Film Thickness |
30-50 |
60-100 |
15,7-10,0 |
| Recommended |
40 |
80 |
12,5 |
| Surface Temperature |
Surface Drying |
Hard Drying 2 |
Second Coat |
Coat 3 |
| Min. |
Max. |
10° C
23° C
|
120 minutes
60 minutes
|
14 hours
6,5 hours
|
14 days
7 days
|
8 hours
4 hours
|
|
|