| Description |
Two component, epoxy-polyamid based undercoat.
|
| Application Areas |
Applied on steel, galvanized steel, and aluminium Surfaces as anti-corrosive undercoat.
|
| Storage |
Should be stored in cool, well ventilated, and prevented from high temperature places.
|
| Package |
20 lt CompA / 5 lt CompB / 1 lt CompA / 0.200 lt CompB
|
 |
| Color |
Gray, red
|
| Solid Matterial (volume) |
% 51 (+/- 2)
|
| Density |
1,1 - 1,4 gr/cm3
|
| Drying Time |
Depends on air circulaiton, environment temperature and film thickness.
|
| Flash Point |
25° C (+/- 2)
|
| Brilliance |
Matt
|
| Color Endurance |
Good
|
 |
| Mixture |
4 volume CompA + 1 volume CompB
|
| Mixture Applicable For |
8 hours (Decreases at high temperatures)
|
| Thinner / Cleaning Solvent |
Epoxy thinner
|
| Airless Pistol Data |
Hydrolic Pressure
(At the jet) |
: 15 Mpa |
| Jet |
: 0,46 - 0,58 mm |
| Spraying Angle |
: 40° - 80° |
| Filter |
: Should be clean. |
|
|
|
 |
| Surface Preparation |
Surfaces must be well cleaned, dry and defectless. Sanding at SQ 2.5 or mechanical cleaning at St 2 recommended.
|
| Application Conditions |
Surface temperature must be at least 3° C higher than the air condensation temperature. Since curing decreases considerably in low temperatures application should be made at least at 10° C .
|
| Recommended Painting System |
Epoxy undercoat: 2x50 micron Epoxy finish paint: 1x50 micron
|
| Working Conditions |
Follow the instructions on the package. Avoid inhaling the vapor directly and avoid contact with skin.
|
| Application Method |
Applied with airless pistol, air pistol or with brush.
|
|
Film Thickness
(Micron/coat) |
Theoretical
Spreading |
| Dry |
Wet |
(m2/lt) |
| Applicable Film Thickness |
40-60 |
80-120 |
12,5-8,4 |
| Recommended |
50 |
100 |
10,1 |
| Surface Temperature |
Surface Drying |
Hard Drying 2 |
Second Coat |
Coat 3 |
| Min. |
Max. |
10° C
23° C
35° C
|
120 minutes
60 minutes
30 minutes
|
14 hours
6,5 hours
4 hours
|
14 days
7 days
3 days
|
8 hours
4 hours
2 hours
|
|
|